Flexcon dermaflex™
p.e.f 32 white h-778
Features and Benefits
- 1/32” white polyethylene foam substrate is soft, lightweight, and provides a sturdy base for electrodes & other monitoring applications
- H-778 adhesive bonds to smooth and textured TPO’s and other low-energy surfaces commonly found in medical devices
- H-778 high-performance adhesive with ultra-high strength for extended wear, such as attachment of long-term wearable devices
- Backed with a 90-lb. moisture stable polycoated layflat release liner suitable for roll form, roll to sheet, and sheet form converting
technical data
Values
|
Thickness (Mils[microns])
|
---|---|
Film
|
31.25 (794) +/- 15%
|
Adhesive
|
1.9-2.1 (48-53) +/- 0.1 (3)
|
Liner
|
6.9 (175) +/- 10%
|
Adhesion properties
Ultimate Peel From
|
Average Oz/In
|
(N/m)
|
---|---|---|
Acrylic
|
Foam Rips
|
Foam Rips
|
Glass
|
Foam Rips
|
Foam Rips
|
Polypropylene
|
Foam Rips
|
Foam Rips
|
Stainless Steel
|
Foam Rips
|
Foam Rips
|
Electrical properties
Property
|
Value
|
Test Method
|
---|---|---|
Expected Shear
|
Room Temp (hours): 50+
|
ASTM D 3654 Method A, a. 1 hr. dwell, b. 1 sq. in. surface, c. 4 lb. load
|
Tack (gm/sq cm)
|
810
|
ASTM D 2979
|
Storage Stability
|
Two years stored at 70°F (21°C) and 50% relative humidity
|
Product ID # FLX068293
All of the descriptive information, the typical performance data, and recommendations for the use of FLEXcon products shall be used only as a guide and do not reflect the specification or specification range for any particular property of the product. Furnishing such information is merely an attempt to assist you after you have indicated your contemplated use and shall in no event constitute a warranty of any kind by FLEXcon. All purchasers of FLEXcon products shall be responsible for independently determining the suitability of the material for the purpose for which it is purchased. No distributor, salesman, or representative of FLEXcon is authorized to give any warranty, guarantee, or make any representation in addition or contrary to the above.