Avery Dennison
MED 6017
Double-Coated Foam
MED 6017 is a double-coated, white, soft, conformable, thin, closedcell polyolefin foam coated on both sides with an acrylic adhesive. This product is designed to adhere medical devices to the skin in surgucal applications. It contains a heavy weight liner with ideal release for kiss cutting, die-cutting and converting.
Typical Application
Designed for adhering to various types of substrates with the objective of combining multiple layers within a product’s design.
Features and Benefits
- Conformable and moisture resistant
- High adhesion to skin
- Die-cuttable
- Gamma and EtO sterilizable
|
Physical Properties (Not intended as a specification.)
|
Test Method**
|
Typical Values*
|
|---|---|---|
|
Peel Adhesion on Polyethylene (PE) - Liner
|
TDS-01
|
0.6 lbf/in 2.5 N/25 mm
|
|
Peel Adhesion on Polyethylene (PE) - Unwind
|
TDS-01
|
0.6 lbf/in 2.5 N/25 mm
|
|
Liner Release
|
TDS-06
|
1.9 oz/in 68 g/25 mm
|
|
Finat Tack - Liner
|
TDS-07
|
6.2 lbf/in 27 N/25 mm
|
|
Finat Tack - Unwind
|
TDS-07
|
6.5 lbf/in 29 N/25 mm
|
|
Static Shear - Liner
|
TDS-12
|
930 minutes
|
|
Static Shear - Unwind
|
TDS-12
|
1030 minutes
|
|
Elongation Machine Direction
|
TDS-15
|
350%
|
|
Elongation Cross Direction
|
TDS-15
|
450%
|
|
Load at Break Machine Direction
|
TDS-15
|
11.0 lbf/in 50 N/ 25mm
|
|
Load at Break Cross Direction
|
TDS-15
|
6.0 lbf/in 27 N/ 25mm
|
|
Product Construction
|
Typical Values*
|
Description
|
|---|---|---|
|
Unwind Adhesive Thickness
|
2.0 mils 50 µm
|
Acrylic adhesive designed for medical applications
|
|
Carrier Thickness
|
62.5 mils 1580 µm
|
White closed cell foam
|
|
Liner Adhesive Thickness
|
2.0 mils 50 µm
|
Acrylic adhesive designed for medical applications
|
|
Release Liner Thickness
|
3.6 mils 90 µm
|
Super-calendered kraft
|
*Refer to product specifications for material acceptance limits. **Test method information available upon request.
STORAGE AND SHELF LIFE
Two years when stored at 23°C (73°F), 50% relative humidity, out of direct sunlight, in original packaging.